I just found on rio that handy flux makes a high temp flux. Type b1.
Now I’ve been using a ‘regular’ flux I had been taught to use and it
is low temp. I dork in nickle, copper and brass. Would I be better
off with a high temp flux to cut back on that heavy oxidation of
copper?
Thank you
Brenda